Advanced Search

Journal Navigation

Journal Home

Subscriptions

Archive

Contact Us

Table of Contents

Sign In to gain access to subscriptions and/or personal tools.
Journal of Biomaterials Applications
This Article
Right arrow Full Text (PDF)
Right arrow References
Right arrow Alert me when this article is cited
Right arrow Alert me if a correction is posted
Services
Right arrow Email this article to a friend
Right arrow Similar articles in this journal
Right arrow Similar articles in PubMed
Right arrow Alert me to new issues of the journal
Right arrow Add to Saved Citations
Right arrow Download to citation manager
Right arrowRequest Permissions
Right arrow Request Reprints
Right arrow Add to My Marked Citations
Citing Articles
Right arrow Citing Articles via Google Scholar
Right arrow Citing Articles via Scopus
Google Scholar
Right arrow Articles by Keyf, F.
Right arrow Articles by Uzun, G.
Right arrow Search for Related Content
PubMed
Right arrow PubMed Citation
Right arrow Articles by Keyf, F.
Right arrow Articles by Uzun, G.
Social Bookmarking
Add to CiteULike   Add to Complore   Add to Connotea   Add to Del.icio.us   Add to Digg   Add to Reddit   Add to Technorati   Add to Twitter  
What's this?

The Effects of Glass Fiber Reinforcement at Different Concentrations on the Transverse Strength, Deflection and Modulus of Elasticity of a Provisional Fixed Partial Denture Resin

Filiz Keyf

Department of Prosthodontics, School of Dentistry, Hacettepe University, Sihhiye 06100, Ankara, Turkey

Gülay Uzun

School of Dental Technology, Hacettepe University, Sihhiye 06100, Ankara, Turkey

This study focused on some mechanical properties such as the transverse strength, maximal deflection and modulus of elasticity of a resin reinforced with untreated, chopped form glass fibers at different concentrations. A Teflon mould was used to prepare four groups of specimens. The specimens were prepared with different concentrations of the glass fiber to the mass of the powder/liquid mix (0.5, 1, 1.5%), and a mix without fiber was used as the control group. All the specimens were subjected to transverse testing with a cross-head speed of 5 mm/min. The load to fracture for each specimen with the maximum deflection at the point of loading in a three-point load test was recorded. The transverse strength of 0.5% fiber concentration was 54.45 MPa. The lowest value was 49.67 MPa for the 1% fiber concentration. The highest mean strength was for the specimens reinforced with 0.5% glass fiber. This mean was higher than for the mean of the control "without fiber" specimens. The specimens demonstrated an insignificant decrease in the transverse strength and the maximum deflection when the fiber concentration was increased. The inclusion of 1% glass fiber reduced the transverse strength, although the result was not statistically significant.

Key Words: glass fiber reinforcement • concentration • provisional fixed partial denture resin

Journal of Biomaterials Applications, Vol. 16, No. 2, 149-156 (2001)
DOI: 10.1106/BGNY-V5DA-VMWB-TC2W